首页> 外文期刊>Journal of industrial and engineering chemistry >Fracture toughness improvement of epoxy resins with short carbon fibers
【24h】

Fracture toughness improvement of epoxy resins with short carbon fibers

机译：短碳纤维环氧树脂的断裂韧性提高

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This study examined the thermal stability and fracture toughness of diglycidylether of bisphenol-A (DGEBA)/short carbon fiber (SCF) composites using several techniques. The thermal stability of the DGEBA/SCF composites was similar to that of neat epoxy resin. The fracture toughness of the composites was significantly improved relative to the neat resin. The SEM micrographs indicated that a relatively rough surface with shear deformation and tortuous cracks was formed, thereby preventing deformation and crack propagation and inducing higher fracture toughness in the DGEBA/SCF composites.
机译：这项研究使用多种技术研究了双酚A（DGEBA）/短碳纤维（SCF）复合材料的二缩水甘油醚的热稳定性和断裂韧性。 DGEBA / SCF复合材料的热稳定性类似于纯环氧树脂。相对于纯树脂，复合材料的断裂韧性明显提高。 SEM显微照片表明，形成了具有剪切变形和曲折裂纹的相对粗糙的表面，从而防止了DGEBA / SCF复合材料的变形和裂纹扩展并诱导了更高的断裂韧性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号