Normal state resistivity of YBa sub(2)Cu sub(3)O sub(7- delta )/PrBa sub(2)Cu sub(2.8)Ga sub(0.2) O sub(7- delta ) c-axis superlattices: Evidence for an underdoping effect of YBa sub(2)Cu sub(3)O sub(7- delta )

机译：YBa sub（2）Cu sub（3）O sub（7- delta）/ PrBa sub（2）Cu sub（2.8）Ga sub（0.2）O sub（7- delta）c轴超晶格的常态电阻率：证据YBa sub（2）Cu sub（3）O sub（7- delta）的欠掺杂效应

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We measured the ab-plane resistivity of c-axis YBa sub(2)Cu sub(3)O sub(7- delta ) /PrBa sub(2)Cu sub(2.8)Ga sub(0.2)O sub(7) superlattices grown by pulsed laser deposition, from T sub(C) to 325 K. The normal-state resistivity and the fluctuation regime above T sub(C) were studied for different thickness of YBa sub(2)Cu sub(3)O sub(7- delta ) and PrBa sub(2)Cu sub(2.8)Ga sub(0.2)O sub(7- delta ) in the superlattice period. As the concentration of PrBa sub(2)Cu sub(2.8)Ga sub(0.2)O sub(7- delta ) is raised, the T sub(C) decreases and the resistivity increases. Evidence is given for an underdoping effect in the YBa sub(2)Cu sub(3)O sub(7- delta ) layers and our measurements are compared to similar measurements on oxygen-deficient YBa sub(2)Cu sub(3)O sub(7- delta ) thin films, grown on the same equipment. They are also compared to measurements on YBa sub(2)Cu sub(3-x)Co sub(x)O sub(7- delta ) single crystals made by other groups. We present here the different measurements and investigate the mechanisms that could be held responsible for this depletion in charge carriers.
机译：我们测量了c轴YBa sub（2）Cu sub（3）O sub（7- delta）/ PrBa sub（2）Cu sub（2.8）Ga sub（0.2）O sub（7）超晶格的ab面电阻率通过脉冲激光沉积生长，从T sub（C）到325K。研究了不同厚度的YBa sub（2）Cu sub（3）O sub（T）的常态电阻率和在T sub（C）之上的涨落状态。 7-delta）和PrBa sub（2）Cu sub（2.8）Ga sub（0.2）O sub（7- delta）在超晶格周期中。随着PrBa sub（2）Cu sub（2.8）Ga sub（0.2）O sub（7-delta）的浓度升高，T sub（C）减小，电阻率增加。给出了YBa sub（2）Cu sub（3）O sub（7-delta）层中掺杂不足的证据，并将我们的测量结果与对氧不足的YBa sub（2）Cu sub（3）O的类似测量结果进行了比较。在同一设备上生长的亚（7-delta）薄膜。它们还与其他小组制作的YBa sub（2）Cu sub（3-x）Co sub（x）O sub（7- delta）单晶的测量结果进行了比较。我们在这里介绍了不同的测量方法，并研究了可能对电荷载流子耗尽负责的机制。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号