首页> 外文期刊>Journal of Macromolecular Science. Pure and Applied Chemistry >Electrosynthesis of Poly(azure B) from Sulfuric Acid Solution
【24h】

Electrosynthesis of Poly(azure B) from Sulfuric Acid Solution

机译：由硫酸溶液电合成聚（天青B）

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Electrochemical polymerization of azure B from sulfuric acid solution was carried out by using cyclic voltammetry. The electrolytic solution consisted of 5.0 mmol · dm-3 azure B and 0.3 mol · dm-3 H2SO4. The temperature for polymerization was controlled at 20°C. A blue film, i.e., poly(azure B) was formed on a platinum foil and had a electrochemical reversibility, stability and a fast charge transfer ability in the 0.5 mol · dm-3 Na2SO4 with pH 4.0 solution. The currents of both anodic and cathodic peaks are proportional to 1/2 at the scan rate () region of 25 and 600 mV · s-1 on the cyclic voltammograms. The conductivity of poly(azure B) is 2.8×10-6 S · cm-1 at 20°C. The UV-visible spectrum and Raman spectrum of the polymer are different from those of the monomer. A possible polymerization mechanism of azure B was also proposed.
机译：使用循环伏安法从硫酸溶液中进行天青B的电化学聚合。电解液由5.0 mmol·dm-3天蓝色B和0.3 mol·dm-3 H2SO4组成。聚合温度控制在20℃。在铂箔上形成蓝色膜，即聚（天青B），在pH值为4.0的0.5 mol·dm-3 Na2SO4中具有电化学可逆性，稳定性和快速的电荷转移能力。在循环伏安图上，在25和600 mV·s-1的扫描速率（）区域，阳极和阴极峰的电流都与1/2成正比。聚（天青B）在20°C下的电导率为2.8×10-6 S·cm-1。聚合物的UV-可见光谱和拉曼光谱与单体的不同。还提出了可能的天青B的聚合机理。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号