High-iron ferric glass

机译：高铁铁玻璃

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

iron commonly exists as an equilibrium mixture of ferrous ions, Fe2+, and ferric ions, Fe3+ in glass. Fe3+ is a strong absorber of ultraviolet light and imparts a yellow color to glass, while Fe2+ has an absorption band in the near-infrared, resulting in a blue coloration. This study synthesized soda-lime-silicate glasses with high iron contents (1-3 wt%) in which virtually all the iron was fully oxidized to the ferric redox state, resulting in a UV-absorbing, yellow glass. The effectiveness of three common oxidizing agents (cerium, manganese, and antimony) to react with Fe2+ in these high-iron glasses was determined as a function of the processing temperature (1200-1400 degrees C). Cerium was the best oxidizer at the highest iron contents (3 wt%), while manganese was more effective at the lowest iron contents (1 wt%). (c) 2006 Elsevier B.V. All rights reserved.
机译：铁通常以亚铁离子Fe2 +和铁离子Fe3 +的平衡混合物形式存在于玻璃中。 Fe 3+是紫外线的强吸收剂，使玻璃具有黄色，而Fe 2+在近红外具有吸收带，从而导致蓝色。这项研究合成了具有高铁含量（1-3重量％）的钠钙硅酸盐玻璃，其中几乎所有铁都被完全氧化为三氧化二铁状态，从而产生了可吸收紫外线的黄色玻璃。确定了这些高铁玻璃中三种常见氧化剂（铈，锰和锑）与Fe2 +反应的效率与处理温度（1200-1400摄氏度）的关系。铈在铁含量最高（3 wt％）时是最好的氧化剂，而锰在铁含量最低（1 wt％）时更有效。 （c）2006 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号