The viscoelasticity of vitrified 3,9-bis{1,1-dimethyl-2[beta-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy]ethyl}-2, 4, 8, 10-tetraoxaspiro [5,5]-undecane (abbreviated as AO-80) during the annealing process was investigated by DMA under the solid shearing model for the first time. The results showed that vitrified AO-80 obtained by quenching from its melting state has super-high damping properties (tan delta > 26), which are much higher than any polymer materials (tan delta < 3). Moreover, the vitrified AO-80 annealed at 80 degrees C under different annealing time has different aggregate structure, resulting in the variation of its viscoelasticity. With the increasing of annealing time the peak value of tan 6 decreased, but still higher than any other polymers. These results also provided the evidences of the damping properties improvement of polymer composites added AO-80. (C) 2007 Elsevier B.V. All rights reserved.
机译：玻璃化的3,9-双{1,1-二甲基-2 [β-（3-叔丁基-4-羟基-5-甲基苯基）丙酰氧基]乙基} -2，4，8，8，10-四氧杂螺的粘弹性[ DMA在固体剪切模型下首次研究了5,5]-十一烷（缩写为AO-80）在退火过程中的作用。结果表明，从熔融态淬火获得的玻璃化AO-80具有超高的阻尼特性（tanδ> 26），远高于任何聚合物材料（tanδ<3）。而且，在不同退火时间，80℃退火的玻璃化AO-80具有不同的聚集体结构，导致其粘弹性变化。随着退火时间的增加，tan 6的峰值降低，但仍高于其他任何聚合物。这些结果也提供了添加AO-80的聚合物复合材料阻尼性能改善的证据。 （C）2007 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号