首页> 外文期刊>Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites >Direct observation of sp(3) bonding in tetrahedral amorphous carbon UV Raman spectroscopy
【24h】

Direct observation of sp(3) bonding in tetrahedral amorphous carbon UV Raman spectroscopy

机译：在四面体无定形碳紫外拉曼光谱中直接观察sp（3）键

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

It is shown that Raman spectroscopy using UV excitation at 244 nm directly reveals the vibrational modes of sp(3) sites in tetrahedral amorphous carbon (ta-C). The spectrum of ta-C consists of two bands around 1100 cm(-1) and 1600 cm(-1), which appear to arise from sp(2) sites and sp(3) sites, respectively. Analysis of the spectra shows that the 1100 cm(-1) mode arises from a coupling to a states and it shifts from about 1400 cm(-1) to 1100 cm(-1) with increasing sp3 content. (C) 1998 Elsevier Science B.V. All rights reserved. [References: 27]
机译：结果表明，使用244 nm紫外线激发的拉曼光谱直接揭示了四面体无定形碳（ta-C）中sp（3）位的振动模式。 ta-C的光谱由大约1100 cm（-1）和1600 cm（-1）的两个波段组成，这两个波段分别来自sp（2）和sp（3）。光谱分析表明，1100 cm（-1）模式是由耦合到状态引起的，并且随着sp3含量的增加，它从大约1400 cm（-1）转变为1100 cm（-1）。 （C）1998 Elsevier Science B.V.保留所有权利。 [参考：27]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号