Evidence for the formation of SiON glasses

机译：形成SiON玻璃的证据

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Novel glasses within the Si-O-N system were synthesized by melting mixtures of crystalline alpha-SiO2 and alpha-Si3N4 in the range from 2.9 to 24 at.% nitrogen. X-ray diffraction (XRD) and Fourier transformation infrared spectroscopy (FT-IR) measurements indicate the formation of ternary phases in an amorphous state. The incorporation of nitrogen into the network structure was proven by Si-29 magic angle spinning nuclear magnetic resonance (MAS-NMR) and Si K-X-ray absorption near edge structure spectroscopic studies which both show. independently. the presence of mixed SiO4-xNx tetrahedra (x = 0, 1, 2, 3, 4). The relative frequency of these units as derived from the deconvolution of Si-29-MAS-NMR spectra is in agreement with a random distribution of nitrogen within the network structure. (C) 1998 Elsevier Science B.V. [References: 40]
机译：Si-O-N体系中的新型玻璃是通过熔化氮含量为2.9至24 at。％的晶体α-SiO2和α-Si3N4的混合物而合成的。 X射线衍射（XRD）和傅立叶变换红外光谱（FT-IR）测量表明，非晶态三元相的形成。均通过Si-29魔角旋转核磁共振（MAS-NMR）和Si K-X射线吸收近边缘结构光谱研究证明了氮原子在网络结构中的结合。独立地。混合的SiO4-xNx四面体（x = 0、1、2、3、4）的存在。由Si-29-MAS-NMR光谱的反卷积得出的这些单元的相对频率与氮在网络结构内的随机分布是一致的。 （C）1998 Elsevier Science B.V. [参考：40]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号