首页> 外文期刊>Applied optics >Femtosecond-laser micromachined optical waveguides in Bi_4Ge_3O_(12) crystals
【24h】

Femtosecond-laser micromachined optical waveguides in Bi_4Ge_3O_(12) crystals

机译：Bi_4Ge_3O_（12）晶体中的飞秒激光微加工光波导

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The optical waveguides in Bi_4Ge_3O_(12) (BGO) crystals in both depressed-cladding and dual-line configurations have been produced using femtosecond-laser micromachining. The guiding properties and thermal stabilities of the BGO waveguides have been investigated for both geometries, showing different performance of the fabricated structures. Both depressed-cladding and dual-line waveguides support guidance along both TE and TM polarizations. Thermal annealing treatments up to 600℃ reduce the propagation loss of dual-line waveguides to as low as 0.5 dB/cm, while the cladding waveguide is only stable under thermal treatment not higher than 260℃, reaching a propagation loss of 2.1 dB/cm.
机译：使用飞秒激光微加工技术制造出了凹陷包层和双线配置的Bi_4Ge_3O_（12）（BGO）晶体中的光波导。已针对两种几何结构研究了BGO波导的导引特性和热稳定性，显示了制造结构的不同性能。凹陷包层波导和双线波导都支持沿TE和TM极化的引导。高达600℃的热退火处理将双线波导的传输损耗降低至0.5 dB / cm，而包层波导仅在不高于260℃的热处理下才稳定，达到2.1 dB / cm的传输损耗。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号