首页> 外文期刊>Asian Journal of Chemistry: An International Quarterly Research Journal of Chemistry >Study on the Influence of Modified Multi-Walled Carbon Nanotubes to the Shear Strength of Urea-Formaldehyde Resin Adhesive
【24h】

Study on the Influence of Modified Multi-Walled Carbon Nanotubes to the Shear Strength of Urea-Formaldehyde Resin Adhesive

机译：改性多壁碳纳米管对脲醛树脂胶粘剂剪切强度影响的研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Multi-walled carbon nanotubes (MWCNTs) were modified successfully with concentrated sulfuric aciditric acid 3:1 (v/v) and anionic surfactant, then MWCNTs/urea-formaldehyde resin (UF) composites were prepared through mechanical mixing and ultrasonic method. The results show that the surface of MWCNTs was introduced carboxyl groups and the hydrophilic groups of-OSO3~(2-) after modification. Shear strength of MWCNTs/UF conposites increased by 90.7 % comparing with pure UF. The optimal proportion of sodium dodecyl sulfate (SDS)/MWCNTs is 2:1 (wt. ratio), which the modified MWCNTs could be dispersive in UF resin, the mixing time decreased by adding surfactant.
机译：用浓硫酸/硝酸3：1（v / v）和阴离子表面活性剂成功修饰了多壁碳纳米管（MWCNTs），然后通过机械混合和超声方法制备了MWCNTs /脲醛树脂（UF）复合材料。结果表明，改性后的碳纳米管表面引入了羧基和-OSO3〜（2-）的亲水基。与纯UF相比，MWCNTs / UF复合材料的剪切强度提高了90.7％。十二烷基硫酸钠（SDS）/ MWCNT的最佳比例为2：1（重量比），该改性的MWCNT可以分散在UF树脂中，通过添加表面活性剂可以减少混合时间。