首页> 外文期刊>RSC Advances >Facile synthesis of TaOxNy photocatalysts with enhanced visible photocatalytic activity
【24h】

Facile synthesis of TaOxNy photocatalysts with enhanced visible photocatalytic activity

机译：简便地合成具有增强的可见光催化活性的TaOxNy光催化剂

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

N-doped TaOxNy is prepared using ethylenediamine as the nitrogen source by a sol-gel method. The obtained samples are subsequently calcined at 500-900 degrees C. XRD analysis and XPS survey indicate the presence of immature TaO2 (Ta4+) in the N-doped TaOxNy sample sintered at 550 degrees C (TaOxNy-550), and the UV results show TaOxNy-550 has a rather strong absorption in the visible light region. The photocatalytic activities of TaOxNy are evaluated in hydrogen generation by water splitting and photodegradation of methyl orange. The N-doped TaOxNy sample sintered at 550 degrees C shows the highest H-2 generation rate of 3.12 mmol g(-1) h(-1), and only 3.1% methyl orange is left after 90 min irradiation. Such photocatalytic activities are comparable to the conventional nitrogen-doped titania.
机译：使用乙二胺作为氮源，通过溶胶-凝胶法制备N掺杂的TaOxNy。随后将获得的样品在500-900摄氏度下煅烧。XRD分析和XPS调查表明，在550摄氏度（TaOxNy-550）烧结的N掺杂TaOxNy样本中存在不成熟的TaO2（Ta4 +）。 TaOxNy-550在可见光区域具有相当强的吸收性。 TaOxNy的光催化活性通过水分解和甲基橙的光降解作用在制氢中进行评估。在550摄氏度下烧结的N掺杂TaOxNy样品显示出最高的H-2生成速率为3.12 mmol g（-1）h（-1），并且在90分钟的照射后仅剩下3.1％的甲基橙。这种光催化活性与常规的氮掺杂二氧化钛相当。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号