首页> 外文期刊>Optics Letters >Transparent conductive oxide layer with monolayer closed-pack Al-doped ZnO spheres and their application to a-Si thin-film solar cells
【24h】

Transparent conductive oxide layer with monolayer closed-pack Al-doped ZnO spheres and their application to a-Si thin-film solar cells

机译：单层密排铝掺杂ZnO球的透明导电氧化物层及其在a-Si薄膜太阳能电池中的应用

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We report a new (to the best of our knowledge) transparent conductive oxide (TCO) layer with a monolayer of closed-pack Al-doped ZnO (AZO) spheres partly embedded in an AZO thin film. The average transmittance and haze ratio in the wavelength range of 380-800nm achieves 65percent and 55percent, respectively, when AZO spheres with a diameter of 500 nm are embedded in a thickness of 240 nm AZO thin films. The a-Si thin-film solar cell with a regular p-i-n TCO structure is demonstrated. Under air mass 1.5 global illumination, conversion efficiencies of 5.6percent, a fill factor of 0.55, V_(oc) of 0.81 V, and a J_(sc) of 2.44 mA/cm~(2) are obtained. The Letter helps us to open up potential applications of a new TCO in advanced solar cells and light-emitting diodes.
机译：我们报告了一个新的（据我们所知）透明导电氧化物（TCO）层，该层具有单层密闭包装的Al掺杂ZnO（AZO）球体，部分嵌入AZO薄膜中。当将直径为500 nm的AZO球嵌入厚度为240 nm的AZO薄膜中时，在380-800nm波长范围内的平均透射率和雾度比分别达到65％和55％。对具有规则的p-i-n TCO结构的a-Si薄膜太阳能电池进行了说明。在空气质量为1.5的全局照明下，转换效率为5.6％，填充系数为0.55，V_（oc）为0.81 V，J_（sc）为2.44 mA / cm〜（2）。这封信帮助我们开拓了新型TCO在先进太阳能电池和发光二极管中的潜在应用。