首页> 外文期刊>Journal of Applied Polymer Science >Crosslinking studies on poly(ethylene terephthalate-co-1,4-phenylene bisacrylate)
【24h】

Crosslinking studies on poly(ethylene terephthalate-co-1,4-phenylene bisacrylate)

机译：聚对苯二甲酸乙二醇酯-co-1,4-亚苯基二丙烯酸酯的交联研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Several compositionally different poly(ethylene terephthalate-co-1,4-phenylene bisacrylate) (PETPBA) copolymers were melt spun into fibers. The resulting fibers were subjected to UV irradiation to induce crosslinking. Evidence of crosslinking was obtained from FTIR, solid-state C-13-NMR, thermal analysis, and solubility. Irradiation of the fiber results in an increased glass-transition temperature, reduced thermal shrinkage, and enhanced modulus retention at elevated temperature. (C) 2003 Wiley Periodicals, Inc. [References: 22]
机译：将几种组成不同的聚对苯二甲酸乙二酯-co-1,4-亚苯基二丙烯酸酯（PETPBA）共聚物熔纺成纤维。使所得纤维经受UV辐射以诱导交联。交联的证据来自FTIR，固态C-13-NMR，热分析和溶解度。纤维的辐照会导致玻璃化转变温度升高，热收缩率降低以及在高温下模量保持率提高。 （C）2003 Wiley Periodicals，Inc. [参考：22]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号