首页> 外文期刊>Acta Crystallographica, Section B. Structural Science >The piezoelectric tensor element d(33) of KTiOPO4 determined by single crystal X-ray diffraction
【24h】

The piezoelectric tensor element d(33) of KTiOPO4 determined by single crystal X-ray diffraction

机译：用单晶X射线衍射测定的KTiOPO4的压电张量元件d（33）

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The d(33) piezoelectric constant of KTiOPO4 (potassium titanium orthophosphate, KTP) has been determined for two different samples and at temperatures between 100 and 220 K, using high-resolution X-ray diffraction of a single crystal in an electric field. The observed value of 15(2) x 10(-12) mV(-1) is between the two values of 10.4 and 25.8 x 10(-12) mV(-1) found in the literature. The value of d(33) is shown to be constant over the temperature range 100-220 K and no anomaly was observed at the conductor-insulator transition at 150 K. The results obtained are believed to be sample-independent, since the same value was obtained for two different crystals, measured at different sources.
机译：使用电场下单晶的高分辨率X射线衍射，已针对两个不同的样品并在100至220 K的温度下确定了KTiOPO4（正磷酸钾钛，KTP）的d（33）压电常数。 15（2）x 10（-12）mV（-1）的观测值介于文献中的10.4和25.8 x 10（-12）mV（-1）的两个值之间。 d（33）的值在100-220 K的温度范围内保持恒定，并且在150 K的导体-绝缘体过渡温度下未观察到异常。由于相同的值，因此得出的结果与样品无关。对于两种不同的晶体，在不同的来源进行了测量，得到的结果。