首页> 外文期刊>Crystal growth & design >High-capacity gas storage by a microporous oxalamide-functionalized NbO-type metal-organic framework
【24h】

High-capacity gas storage by a microporous oxalamide-functionalized NbO-type metal-organic framework

机译：通过微孔草酰胺官能化的NbO型金属-有机骨架进行大容量气体存储

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A microporous oxalamide-functionalized NbO-type metal-organic framework, HNUST-3, has been designed and synthesized by self-assembling [Cu_ 2(COO)_4] paddlewheel SBUs and a novel tetracarboxylate ligand with linking oxalamide groups. HNUST-3 represents the first example of a porous oxalamide-functionalized MOF, which exhibits a high BET surface area of 2412 m~2·g~(-1), large H_2 uptake (unsaturated total capacity of 6.1 wt % at 20 bar and 77 K), and excellent CH_4 storage (135.8 cm~3(STP)cm~(-3) at 20 bar and 298 K) as well as high CO_2 adsorption capacity (20.2 mmol·g~(-1) at 20 bar and 298 K) with good selectivity for CO_2 over CH_4 (7.9) and N_2 (26.1) at 298 K.
机译：通过自组装[Cu_2（COO）_4]桨轮SBU和具有连接草酰胺基的新型四羧酸酯配体，设计并合成了微孔草酰胺官能化的NbO型金属有机骨架HNUST-3。 HNUST-3代表了多孔草酰胺官能化的MOF的第一个实例，它具有2412 m〜2·g〜（-1）的高BET表面积，大的H_2吸收率（在20 bar下不饱和的总容量为6.1 wt％）和77 K），出色的CH_4存储（20 bar和298 K时135.8 cm〜3（STP）cm〜（-1）和20 bar和20 bar时高的CO_2吸附能力（20.2 mmol·g〜（-1） 298 K），在298 K时对CH_2（7.9）和N_2（26.1）的CO_2具有良好的选择性。