首页> 外文期刊>Corrosion Engineering, Science and Technology >Electrochemical study on corrosion behaviour of zircaloy-2 in aqueous medium containing permanganate ion
【24h】

Electrochemical study on corrosion behaviour of zircaloy-2 in aqueous medium containing permanganate ion

机译：Zircaloy-2在高锰酸根离子水介质中腐蚀行为的电化学研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The corrosion compatibility of zircaloy-2 was studied in strong oxidising permanganate based acidic (HMnO_4) medium using impedance spectroscopy and potentiodynamic anodic polarisation methods at room temperature (28℃) and elevated temperatures (65 and 90℃). The average corrosion rate of zircaloy-2 in HMnO_4 medium (0·417-8·33 mM) was found to be 1·32 × 10~(-4) μm h~(-1) at 28℃, 2·59 × 10~(-4) μm h~(-1) at 65℃ and 3·53 × 10~(-4) μm h~(-1) at 90℃. At 28℃, the polarisation resistance R_p values obtained from impedance spectrum were higher (in kΩ) when compared to R_p values at 65 and 90℃, indicating a lower corrosion rate at lower temperature. Comparative studies with 2·5 mM H_2SO_4 and platinum (as a working electrode) showed the effects of oxidising nature and participation of additional redox reactions in HMnO_4 medium. Cyclic polarisation studies showed the absence of pitting attack on zircaloy-2.
机译：在室温（28℃）和高温（65℃和90℃）下，采用阻抗谱和电位动力学阳极极化方法，研究了Zircaloy-2在强氧化高锰酸盐基酸性（HMnO_4）介质中的腐蚀相容性。在28℃，2·59×下，在HMnO_4介质（0·417-8·33 mM）中Zircaloy-2的平均腐蚀速率为1·32×10〜（-4）μmh〜（-1）。 65℃时为10〜（-4）μmh〜（-1），90℃时为3·53×10〜（-4）μmh〜（-1）。在28℃时，与在65℃和90℃时的R_p值相比，从阻抗谱获得的极化电阻R_p值较高（以kΩ为单位），表明较低温度下的腐蚀速率较低。与2·5 mM H_2SO_4和铂（作为工作电极）的比较研究表明，氧化性质的影响以及HMnO_4介质中其他氧化还原反应的参与。循环极化研究表明没有对Zircaloy-2产生点蚀。