Phase Formation, Structure, and Electrical Conductivity of Modified Lanthanum-Gallate Ceramics

机译：改性镧 - 粘滞陶瓷的相形成，结构和导电性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The solid-phase synthesis method is used to prepare perovskite-like ceramic samples with the compositions (La~(0.8)Sr~(0.2)){[Ga~(0.8– x )(Si~(0.5)Mg~(0.5))~( x )]Mg~(0.2)}O~(3– y )( x = 0, 0.1, 0.2, 0.4, and 0.6) and investigate their phase formation, structure, microstructure, and electrical conductivity. Single-phase samples are obtained when up to 10 at % of gallium cations are replaced with silicon and magnesium cations. It is established that silicon-containing samples with the perovskite structure are characterized by a high density, optimal microstructure, dense grain packing, and large electrical conductivities at high temperatures.
机译：固相合成方法用于使用组合物制备钙钛矿状陶瓷样品（La〜（0.8）Sr〜（0.2））{[Ga〜（0.8- x）（Si〜（0.5）mg〜（0.5） ）〜（x）] Mg〜（0.2）} O〜（3- y）（x = 0,0.1,0.2,0.4和0.6），并研究其相形成，结构，微观结构和电导率。 当高达10at以1％的镓阳离子取代硅和镁阳离子时，获得单相样品。 建立含有钙钛矿结构的含硅样品的特征在于高密度，最佳的微观结构，致密的颗粒包装和高温下的大电导率。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号