首页> 外文期刊>International Journal of Refractory Metals & Hard Materials >Corrosion synthesis of boron carbide with pore and hollow structure
【24h】

Corrosion synthesis of boron carbide with pore and hollow structure

机译：孔和中空结构碳化硼的腐蚀合成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this study, corrosion synthesis of boron carbide particles with pore size ranging from hundreds of nanometers to several micrometers was reported. Firstly, the pristine boron carbide powders which contain free carbon have been synthesized at 350 °C in a steel autoclave. As the pristine boron carbide was refluxed by HC10_4 at 170 °C for 1-2 h, the boron carbide particles with macropores were produced. Similarly, the boron carbide nanocages can also be obtained. The corrosion of the embedded amorphous and/or low crystallinity carbon/boron carbide using HC10_4 was considered for the formation of boron carbide with macropores and hollow nanocages.
机译：在这项研究中，据报道腐蚀合成的碳化硼颗粒的孔径范围从几百纳米到几微米。首先，已在钢制高压釜中于350°C合成了含有游离碳的原始碳化硼粉末。当原始碳化硼在HC10_4中于170°C回流1-2小时后，生成了具有大孔的碳化硼颗粒。类似地，也可以获得碳化硼纳米笼。考虑使用HC10_4腐蚀嵌入的无定形和/或低结晶度的碳/碳化硼，以形成具有大孔和空心纳米笼的碳化硼。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号