首页> 外文期刊>Materials and Manufacturing Processes >Synthesis of β-SiC Powder from Bamboo Leaf in a DC Extended Thermal Plasma Reactor
【24h】

Synthesis of β-SiC Powder from Bamboo Leaf in a DC Extended Thermal Plasma Reactor

机译：直流扩展热等离子体反应器中竹叶合成β-SiC粉末

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Fine silicon carbide powder was synthesized from bamboo leaf in a DC thermal plasma reactor through a single step process. With an applying current of 300 amp and 50 V voltages, the optimum duration of conversion of silica rich bamboo leaf to silicon carbide is 20 minutes. X-ray diffraction (XRD) results reveal that the final product is identified as β-SiC having lattice parameter a = 4.295 A, which is in close agreement with the reported value of 4.347 A. The scanning electron microscope (SEM) micrograph clearly shows the formation of cubical particles of β-SiC. The micro-Raman and X-ray photoelectron spectroscopy (XPS) analysis also confirm the formation of β-SiC phase.
机译：通过直流热等离子体反应器中的竹叶，通过一步法合成了精细的碳化硅粉末。在300安培的电流和50 V的电压下，富含二氧化硅的竹叶转化为碳化硅的最佳持续时间为20分钟。 X射线衍射（XRD）结果表明，最终产物被鉴定为晶格参数a = 4.295 A的β-SiC，与报道的4.347 A值非常吻合。扫描电子显微镜（SEM）显微照片清楚地表明β-SiC的立方颗粒的形成。显微拉曼和X射线光电子能谱（XPS）分析也证实了β-SiC相的形成。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号