首页> 外文期刊>Materials at High Temperatures >High temperature corrosion performance of Q235 steel in sulfur-bearing solution
【24h】

High temperature corrosion performance of Q235 steel in sulfur-bearing solution

机译：Q235钢在含硫溶液中的高温腐蚀性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The high temperature corrosion performance of Q235 steel in sulfur-bearing solutions as a function of temperature, test time, and sulfur content was investigated by weight loss measurements in this study. The results indicate that the corrosion behavior of Q235 steel in sulfur-bearing solution is directly related to the experimental temperature, immersion time and sulfur content. Higher temperature leads to a higher corrosion rate of the steel. The corrosion rate increases during the initial test time and then decreases with increasing the test time. As the sulfur content increases in the solution, the corrosion rate increases, and further increasing the sulfur content leads to a decreased corrosion rate.
机译：本文通过失重测量研究了Q235钢在含硫溶液中的高温腐蚀性能随温度，测试时间和硫含量的变化。结果表明，Q235钢在含硫溶液中的腐蚀行为与实验温度，浸渍时间和硫含量直接相关。较高的温度导致钢的较高的腐蚀速率。腐蚀速率在初始测试时间内会增加，然后随着测试时间的增加而降低。随着溶液中硫含量的增加，腐蚀速率增加，并且硫含量的进一步增加导致腐蚀速率降低。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号