首页> 外文期刊>Nanotechnology >Single-crystal AlN nanonecklaces
【24h】

Single-crystal AlN nanonecklaces

机译：单晶AlN纳米项链

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Distinct single-crystal aluminum nitride nanonecklaces with uniform {10 (1) over bar1} faceted beads are synthesized via catalyst- assisted nitriding of Al. The detailed morphology and structure of the nanonecklaces have been characterized. The growth process has been investigated by comparing the products obtained at different synthesis times. The results reveal that the formation of the nanonecklaces is via a process consisting of facet formation and bead unification. The formation of the {10 (1) over bar1} facets is due to the presence of a liquid phase that lowers the surface tension of otherwise high- energy {10 (1) over bar1} planes. The bead unification is driven by minimizing the energy contributed by surface energy and electrostatic energy. The unique morphology of the nanonecklaces could be useful for studying fundamental physical phenomena and fabricating nanodevices.
机译：通过在催化剂上辅助氮化的Al合成了在bar1}上具有均匀{10（1）}刻面珠的独特的单晶氮化铝纳米项链。已经表征了纳米项链的详细形态和结构。通过比较在不同合成时间获得的产物，研究了生长过程。结果表明，纳米项链的形成是通过小平面形成和珠粒统一的过程。 {10（1）在bar1}面上的形成是由于液相的存在，该液相降低了高能量{10（1）在bar1}平面上的表面张力。通过最小化表面能和静电能贡献的能量来驱动磁珠统一。纳米项链的独特形态可用于研究基本的物理现象和制造纳米器件。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号