摘要

A unique sandwich structure of Ni3S2/RGO/Ni3S2 consisting of Ni3S2 nanosheets was designed and constructed on nickel foam (NF) by a one-step hydrothermal process. The lower Ni3S2 layer was converted in situ from the Ni foam substrate, while the upper Ni3S2 layer with vertical nanosheets resulted from Ni2+ ions in the solution. This Ni3S2/RGO/Ni3S2/NF nanocomposite was directly utilized as a supercapacitor electrode, which possessed a high areal mass loading of 5.2 mg cm(-2), and superior performance: a specific capacitance of up to 16.82 F cm(-2) (i.e., 3234.62 F g(-1)) at a current density of 20 mA cm(-2) (3.85 A g(-1)) and 90% retention of the initial capacitance after 1000 cycles at the high rate of 100 mA cm(-2) (19.23 A g(-1)).
机译：通过一步水热法，在泡沫镍（NF）上设计并构建了由Ni3S2纳米片组成的Ni3S2 / RGO / Ni3S2独特的三明治结构。下部Ni3S2层从Ni泡沫基材上原位转化，而具有垂直纳米片的上部Ni3S2层由溶液中的Ni2 +离子产生。该Ni3S2 / RGO / Ni3S2 / NF纳米复合材料直接用作超级电容器电极，具有5.2 mg cm（-2）的高单位面积质量负载和卓越的性能：比电容高达16.82 F cm（-2） （即3234.62 F g（-1））在20 mA cm（-2）（3.85 A g（-1））的电流密度下，在以100 mA的高速率进行1000次循环后初始电容保持90％ cm（-2）（19.23 A g（-1））。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号