首页> 外文期刊>RSC Advances >Azo-bridged covalent porphyrinic polymers (Azo-CPPs): synthesis and CO2 capture properties
【24h】

Azo-bridged covalent porphyrinic polymers (Azo-CPPs): synthesis and CO2 capture properties

机译：偶氮桥共价卟啉聚合物（Azo-CPPs）：合成和CO2捕获性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A series of azo-bridged, aromatic, nitrogen-rich, microporous covalent porphyrinic polymers (Azo-CPPs) were synthesized through a metal catalyst-free direct coupling of a kind of tetranitro building block, 4NO(2)TPP, and several diamine or tetraamine compounds, under basic conditions. The Azo-CPPs were all amorphous and exhibited surface areas between 197 to 591 m(2) g(-1). The effect of building blocks on the pore properties was discussed. Meanwhile, the capacity of adsorption of CO2 for all the Azo-CPPs was studied and the CO2 uptake capacity was between 7.36% and 9.22% at 273 K and 1.10 bar. The CO2/N-2 selectivities were measured between 27.4-53.9 at 273 K and 31.2-107.8 at 303 K, respectively, showing an increase in selectivity with increasing temperature.
机译：通过无金属催化剂的四硝基结构单元，4NO（2）TPP和几种二胺或四胺的直接偶联，合成了一系列偶氮桥键，芳香族，富氮，微孔共价卟啉聚合物（Azo-CPPs）。四胺化合物，在碱性条件下。偶氮CPPs都是无定形的，并显示197至591 m（2）g（-1）之间的表面积。讨论了砌块对孔隙性能的影响。同时，研究了所有偶氮CPPs的CO 2吸附能力，在273 K和1.10 bar下的CO 2吸收能力在7.36％和9.22％之间。在273 K下测得的CO2 / N-2选择性介于303 K下的27.4-53.9和303 K下的31.2-107.8之间，表明选择性随温度升高而增加。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号