首页> 外文期刊>Scripta materialia >Effects of substituting rare-earth elements for scandium in a precipitation-strengthened Al-0.08at. percent Sc alloy
【24h】

Effects of substituting rare-earth elements for scandium in a precipitation-strengthened Al-0.08at. percent Sc alloy

机译：在沉淀强化的Al-0.08at中用稀土元素替代scan的效果。百分比Sc合金

获取原文
获取原文并翻译 | 示例
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The microhardness of Al-0.06 Sc-0.02 RE alloys (at. percent, with RE (rare-earth) = Dy, Er, Gd, Sm, Y, or Yb) is measured as a function of aging time at 300 deg C. As compared to Al-0.08 Sc, the ternary alloys exhibit: (i) the same incubation time, except for Al-0.06 Sc-0.02 Yb which hardens much faster; (ii) the same or reduced peak microhardnesses (which are higher than for Al-0.06 Sc); and (iii) the same over-aging behavior. All REs segregate to the core of Al_3(Sc_(1-x)RE_x) precipitates.
机译：测量Al-0.06 Sc-0.02 RE合金的显微硬度（百分数，RE（稀土）= Dy，Er，Gd，Sm，Y或Yb）与300℃时效时间的关系。与Al-0.08 Sc相比，三元合金具有：（i）相同的保温时间，但Al-0.06 Sc-0.02 Yb的硬化速度更快; （ii）相同或降低的峰值显微硬度（高于Al-0.06 Sc的峰值显微硬度）; （iii）相同的过度老化行为。所有RE都分离到Al_3（Sc_（1-x）RE_x）沉淀的核心。