摘要

The magnetic properties of two types of poly[(3-methoxy)4,6-toluene] (P3mt_1 and P3mt_2) are studied before and after doping with iodine or organic acids (CF_3COOH or CH_3SO_3H) in a range of temperature varying from 110 to 460 K. Under 250 K and independent of the state, the magnetic susceptibility chi obeys Curie law dependence. Up to this temperature, chi is governed by a Pauli law contribution. This fact can be related to localized or delocalized spin. Furthermore, iodine doping induces distortion in the polymers that affects the ESR line distribution. In the case of organic acids doping process, a hyperfine structure with hyperfine coupling constant values between 2.2 and 2.8 G is observed. As the spin concentration decreases, we deduce that in the case of P3mt_2, there is a de-doping process.
机译：研究了两种类型的聚[（3-甲氧基）4,6-甲苯]（P3mt_1和P3mt_2）在掺杂碘或有机酸（CF_3COOH或CH_3SO_3H）之前和之后在110至200℃的温度范围内的磁性。 460K。在250 K下且与状态无关，磁化率chi服从居里定律。在此温度下，chi受Pauli法则的约束。这个事实可能与局部或非局部自旋有关。此外，碘掺杂会引起聚合物变形，从而影响ESR线的分布。在有机酸掺杂过程中，观察到超细结构的超细偶合常数值在2.2和2.8 G之间。随着自旋浓度的降低，我们推断出在P3mt_2的情况下，存在去掺杂过程。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号