首页> 外文期刊>Philosophical Magazine Letters >A new 1/1 crystal approximant to the stable Ti-Zr-Ni icosahedral quasicrystal
【24h】

A new 1/1 crystal approximant to the stable Ti-Zr-Ni icosahedral quasicrystal

机译：与稳定的Ti-Zr-Ni二十面体准晶体近似的新的1/1晶体

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We report here the discovery of a new bcc 1/1 crystal approximant (W-phase) to the stable icosahedral quasicrystal (i-phase) discovered recently in Ti-Zr-Ni alloys. As-cast Ti-Zr-Ni ingots, which originally contain only the C14 Laves and the hcp solid-solution phases, transform almost completely to the i-phase after annealing at 570oC for 64 h. Anneals at higher temperature (610oC) lead to the formation of the bcc W-phase, with a = 1.432 nm. Preliminary X-ray 0 diffraction studies indicate that the structure of the W-phase is similar to that of the Al-Mg-Zn Bergman phase, or the isostructural Al-Li-Cu R-phase, supporting a previous proposal that i-(Ti-Zr-Ni) is structurally different from i-(Ti-Cr-Si-O) or i-(Ti-Mn-Si-O), but similar to i-(Al-Li-Cu) or i-(Al-Mg-Zn).
机译：我们在这里报告的是，最近在Ti-Zr-Ni合金中发现的稳定的二十面体准晶体（i相）的新bcc 1/1晶体近似（W相）的发现。最初仅包含C14 Laves和hcp固溶相的铸态Ti-Zr-Ni锭在570oC退火64 h后几乎完全转变为i相。高温（610oC）退火导致形成bcc W相，其a = 1.432 nm。初步的X射线0衍射研究表明，W相的结构类似于Al-Mg-Zn Bergman相或同构Al-Li-Cu R相的结构，支持了先前的i-（ Ti-Zr-Ni）在结构上不同于i-（Ti-Cr-Si-O）或i-（Ti-Mn-Si-O），但与i-（Al-Li-Cu）或i-（ Al-Mg-Zn）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号