YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved. [References: 14]
机译：由1-3 nm厚和40 nm宽的颗粒组成的YBCO纳米粉已用于制造覆银超导带。在945°C的氮气中退火10公顷的临界电流为5.02 A（3300 A / cm（2））之后，还在氧气和氮气的混合气氛中进行了退火，该程序生产的胶带的临界电流为2.83 A（2200 A / cm（2））。这些磁带在磁场中显示出非常好的特性。 （C）2002 Elsevier Science B.V.保留所有权利。 [参考：14]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号