The effects of the Sr-for-Ba substitution on the H-irr characteristics of the Cu(Ba1-ySry)(2)YbCu2O6+z (Cu-1212) system is established at two different oxygen-content levels in the range of 0.0 less than or equal to y less than or equal to 0.4. In the fully oxygenated sample series, an optimum was seen at y = 0.2 so that the H-irr line of the present Cu(Ba0.8Sr0.2)(2)YbCu2O6.96 sample clearly exceeds that of the CuBa2YCu2O6.92 compound. For the oxygen-deficient sample series, the H-irr characteristics was depressed with increasing Sr content even though the unit cell decreased. Thus, the H-irr characteristics is mostly controlled by other factors than the thickness of the nonsuperconductive blocking block. (C) 2000 Elsevier Science B.V. All rights reserved. [References: 13]
机译：在0.0范围内的两个不同氧含量水平下，建立了Sr-for-Ba替代对Cu（Ba1-ySry）（2）YbCu2O6 + z（Cu-1212）体系的H-irr特性的影响小于或等于y小于或等于0.4。在完全氧化的样品系列中，在y = 0.2处观察到最佳值，因此当前Cu（Ba0.8Sr0.2）（2）YbCu2O6.96样品的H-irr线明显超过CuBa2YCu2O6.92化合物的H-irr线。对于缺氧样品系列，即使晶胞减少，H-irr特性也会随着Sr含量的增加而降低。因此，除了非超导阻挡块的厚度以外，H-irr特性主要由其他因素控制。 （C）2000 Elsevier Science B.V.保留所有权利。 [参考：13]