FORMATION OF FILM EXCELLENT IN HEAT RESISTANCE, WEAR RESISTANCE, AND SLIDING RESISTANCE ON TITANIUM OR TITANIUM ALLOY
FORMATION OF FILM EXCELLENT IN HEAT RESISTANCE, WEAR RESISTANCE, AND SLIDING RESISTANCE ON TITANIUM OR TITANIUM ALLOY
展开▼
机译:钛或钛合金的耐热性,耐磨性和抗滑性优异的膜的形成
展开▼
页面导航
摘要
著录项
相似文献
摘要
PURPOSE:To improve heat resistance, wear resistance, and sliding resistance by pickling the surface of a Ti metal, exerting Cu or Ni striking, further performing electroplating with Ni or Ni-P alloy, carrying out vacuum heating and surface activation treatment, forming a heat-and wear-resisting film, roughening the surface, and then forming a solid lubricant film on the above surface. CONSTITUTION:After the surface of Ti or Ti alloy is pickled with an aqueous solution of hydrochloric acid and cleaned, Cu or Ni striking is formed to 1-5mum thickness. Subsequently, The above surface of electroplated with Ni or Ni-P alloy to 5-20mum thickness, heated at 450 deg.C for 1hr in a vacuum of 10-1-10-1 Torr to undergo the formation of Ti-Ni or Ti-Cu alloy layer, air-cooled under reduced pressure, and then treated with HF or HNO3 containing aqueous solution to undergo surface activation. Successively, a heat-and wear-resisting film in which Ni-P alloy or Co is used as a matrix and hard pulverized powder of SiC, etc., is dispersed, is formed by an electroplating method, and the surface is formed into rough surface of 1.0-10.0mum RZ by means of the projection of alumina powder, and then, a solid lubricant film of MoS2, graphite, BN, etc., is formed to 5-30mum thickness.
展开▼