A fundamental study has been conducted on Fe$-78$/B$-13$/Si$-9$/ metallic thin film in order to understand the change of the properties and structures of the film as a function of Cr and Ni-Mo additions. The separate additions of Cr and Ni-Mo were successful in the way two new metallic thin films were produced. The composition of the new films are Fe$-77$/Cr$-2$/B$-16$/Si$- 5$/ and Fe$-74$/Ni$-4$/ Mo$-3$/B$-17$/Si$-2$/. Therefore, the study was focussed on evaluating the physical and magnetic properties of the films with respect to the Cr, and Ni-Mo additions. Furthermore, characterizations of the internal and surface structures of the films have been conducted by a Transmission Electron Microscope (TEM) and a Scanning Tunneling Microscope (STM), respectively. A comparison between the internal and surface structures of the films was carried out on both amorphous and crystallined forms. As a result, a correlation between the properties and structures of the films is established.
展开▼
机译：在FE $ -78 $ / B $ -13 $ / SI $ -9下进行了一项基本研究，以了解薄膜的性能和结构的变化作为CR和NI-的功能发作。在制备两个新的金属薄膜的方式中，Cr和Ni-Mo的单独添加是成功的。新电影的组成是FE $ -77 $ / CR $ -2 $ / b $ -11 $ / si $ - 5 $ /和fe $ -74 $ / ni $ -4 $ / mo $ -3 $ / b $ -17 $ / si $ -2 $ /。因此，本研究侧重于评估薄膜的物理和磁性相对于Cr，以及Ni-Mo添加。此外，薄膜的内部和表面结构的特征已经通过透射电子显微镜（TEM）和扫描隧穿显微镜（STM）进行。在无定形和结晶的形式上进行膜的内部和表面结构之间的比较。结果，建立了膜的性质和结构之间的相关性。
展开▼