首页> 外文期刊>Zeitschrift fur Anorganische und Allgemeine Chemie >Ca _2Ga _3MgN _5 - A highly condensed nitridogallate
【24h】

Ca _2Ga _3MgN _5 - A highly condensed nitridogallate

机译：Ca _2Ga _3MgN _5-高度缩合的亚硝基没食子酸酯

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The nitridogallate Ca _2Ga _3MgN _5 was obtained from reaction of the elements in sodium flux with Na-azide at 760 °C in weld shut niobium ampoules. Crystal structure solution and refinement was carried out on the basis of single-crystal X-ray diffraction data. Ca _2Ga _3MgN _5 [space group C2/m (no. 12), a = 11.160(2), b = 3.2965(7), c = 8.006(2) ?, and β = 109.93(3)°, Z = 2] shows an anionic substructure made up of mixed (Mg/Ga)N _4 tetrahedra, which are sharing both common vertices and edges building a three-dimensional network. The crystal structure of Ca _2Ga _3MgN _5 is related to known alkaline earth nitridosilicates (M II _2Si _5N _8, M ~(II) = Sr, Ba), but is significantly higher condensed due to additional edge-sharing in the anionic substructure.
机译：亚硝基没食子酸盐Ca _2Ga _3MgN _5是由钠焊剂中的元素与叠氮化钠在760°C的焊接闭口安瓿瓶中反应制得的。基于单晶X射线衍射数据进行晶体结构的溶解和细化。 Ca _2Ga _3MgN _5 [空间组C2 / m（编号12），a = 11.160（2），b = 3.2965（7），c = 8.006（2）α，β= 109.93（3）°，Z = 2图1显示了由混合的（Mg / Ga）N _4四面体组成的阴离子亚结构，它们共享共同的顶点和共同构成三维网络的边缘。 Ca _2Ga _3MgN _5的晶体结构与已知的碱土金属氮化硅酸盐（M II _2Si _5N _8，M〜（II）= Sr，Ba）有关，但由于阴离子亚结构中的附加边缘共享，其凝结性更高。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号