首页> 外文期刊>Zeitschrift fur Anorganische und Allgemeine Chemie >Synthesis, crystal structure and properties of RbMnO2
【24h】

Synthesis, crystal structure and properties of RbMnO2

机译：RbMnO2的合成，晶体结构与性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

RbMnO2 was prepared via the azideitrate route. Stoichiometric mixtures of the precursers (Mn2O3, RbN3 and RbNO3) were heated in a special regime up to 600 C and annealed at this temperature for 30 h in specially designed silver crucibles. Single crystals have been grown by annealing a 1:1 mixture of Rb2O and MnOx at 585 C for 1200 h. According to the crystal structure determination Mn3+ is in a square-pyramidal coordination by oxygen. These [MnO5] units form double chains extending along the crystallographic c-axis. RbMnO2 shows Curie-Weiss behaviour down to similar to 100 K. A fit of the susceptibility data yields an average value of the magnetic moment (per manganese atom) of mu(eff) = 5.33 mu(B), and theta(P) = -820 K. At 50 K and low field strength onset of ferromagnetic order due to spin canting has been observed.
机译：通过叠氮化物/硝酸盐路线制备RbMnO 2。将前体的化学计量混合物（Mn2O3，RbN3和RbNO3）以特殊方式加热到600℃，并在此温度下在专门设计的银坩埚中退火30小时。通过在585℃下将1：1的Rb2O和MnOx混合物退火1200 h，可以生长出单晶。根据晶体结构的确定，Mn 3+被氧以正方形-金字塔形配位。这些[MnO5]单元形成沿着晶体学c轴延伸的双链。 RbMnO2的居里-魏斯行为低至接近100K。磁化率数据的拟合得出的磁矩（每个锰原子）的平均值为mu（eff）= 5.33 mu（B），theta（P）= -820K。在50 K和低场强下，已经观察到由于自旋倾斜引起的铁磁有序出现。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号