首页> 外文期刊>Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites >Synthesis and characterization of non-crystalline mesoporous silicon oxynitride MCM-41 with high nitrogen content
【24h】

Synthesis and characterization of non-crystalline mesoporous silicon oxynitride MCM-41 with high nitrogen content

机译：高氮含量非晶态介孔氮氧化硅MCM-41的合成与表征

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Mesoporous silicon oxynitrides MCM-41 are synthesized successfully. The resulting materials show not only high nitrogen con.. tent, but also have good structural characteristics of MCM-41 (high surface area, narrow pore size distribution, and good order). The composition and structure of the materials were investigated by CNH analysis, IR spectra, Si-29 MAS NMR CP spectra, XRD, high-resolution TEM and N-2 sorption measurements. Mesoporous silicon oxynitrides MCM-41 are still amorphous after nitridatior at high temperature and for a long time. (c) 2005 Published by Elsevier B.V.
机译：成功合成了介孔氮氧化硅MCM-41。所得材料不仅显示出高氮含量，而且具有MCM-41的良好结构特征（高表面积，狭窄的孔径分布和良好的有序性）。通过CNH分析，IR光谱，Si-29 MAS NMR CP光谱，XRD，高分辨率TEM和N-2吸附测量研究了材料的组成和结构。介孔氮氧化硅MCM-41在高温下经过长时间氮化后仍然是无定形的。 （c）2005年由Elsevier B.V.