The internal friction technique was applied to investigate the structure properties of liquid AsxTe1-x mixtures, A well-pronounced peak was observed in the curve of internal friction as a function of temperature in the liquid AsxTe1-x (x <= 40 at.%), suggesting that an abnormal structural change may take place in this system. The appearance of this internal friction peak during both heating and cooling processes indicates that the abnormal behavior is reversible in the molten As-Te system. Further analysis indicates that the internal friction peak observed in AsxTe1-x (x <= 40 at.%) melts may be associated with the decomposition of AS(2)Te(3) clusters with the increase in temperature. (C) 2007 Elsevier B.V. All rights reserved.
机译：内摩擦技术用于研究液态AsxTe1-x混合物的结构特性，在液态内AsxTe1-x的内摩擦曲线中观察到一个明显的峰值，随温度变化（x <= 40 at。％ ），表明该系统可能发生异常的结构变化。在加热和冷却过程中都出现该内部摩擦峰，表明在熔融的As-Te系统中异常行为是可逆的。进一步的分析表明，随着温度的升高，在AsxTe1-x（x <= 40 at。％）熔体中观察到的内部摩擦峰可能与AS（2）Te（3）团簇的分解有关。 （C）2007 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号