首页> 外文期刊>Journal of Applied Polymer Science >Melt Functionalization of Linear Low-Density Poly(ethylene) with Succinimide and N-Hydroxy Succinimide by Thermolysis Method
【24h】

Melt Functionalization of Linear Low-Density Poly(ethylene) with Succinimide and N-Hydroxy Succinimide by Thermolysis Method

机译：琥珀酰亚胺和N-羟基琥珀酰亚胺通过热解法熔融制备线性低密度聚乙烯

获取原文
获取原文并翻译 | 示例
       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Linear low-density polyethylene (LLDPE) was functionalized with succinimide under different experimental conditions like change in time, temperature, and (% weight of succinimide). The FTIR Spectrum inferred that melt grafting of succinimide onto LLDPE followed the 0.50 order of reaction with respect to (% weight of succinimide). DSC was used to analyze the (melting temperature) T-m and (crystallization temperature) T-c values of functionalized LLDPE. Free radical mechanism explained the formation of nitroxide radical during the melt functionalization of N-hydroxy succinimide (NHS) with LLDPE in the presence of dicumyl peroxide.
机译：线性低密度聚乙烯（LLDPE）在不同的实验条件下（例如时间，温度变化和（琥珀酰亚胺的重量百分比））用琥珀酰亚胺官能化。 FTIR光谱推断，相对于（琥珀酰亚胺的重量％），琥珀酰亚胺的熔融接枝到LLDPE上遵循0.50级的反应。 DSC用于分析官能化的LLDPE的（熔融温度）T-m和（结晶温度）T-c值。自由基机理解释了在过氧化二枯基存在下，用LLDPE对N-羟基琥珀酰亚胺（NHS）进行熔融官能化时，氮氧化物自由基的形成。