Au nanoparticles dispersed cobalt monoxide (CoO) composite films were fabricated via a chemical solution approach combined with a spin-coating processing. Au particles were spherical approximately and uniformly dispersed in the amorphous CoO matrix. The mean diameters of Au particles in the Au/CoO thin films with 40 mol% Au are about 30 nm. The optical absorption peaks due to the surface plasmon resonance (SPR) of Au particles were observed in the UV-vis absorption spectra in the wavelength range of 550-650 nm. The SPR peaks exhibit a red shift and intensify with increasing Au content from 10 to 40 mol%, but show a blue shift and weaken from 40 to 60 mol%. The band gap E_g decreases with increasing Au contents from 10 to 40 mol% but increases by further increasing Au content.
机译：通过化学溶液法与旋涂工艺相结合，制备了金纳米颗粒分散的一氧化钴（CoO）复合薄膜。 Au颗粒近似球形，均匀地分散在非晶态的CoO基体中。具有40mol％的Au的Au / CoO薄膜中的Au颗粒的平均直径为约30nm。在550-650nm波长范围内的UV-vis吸收光谱中观察到由于Au颗粒的表面等离子体激元共振（SPR）引起的光吸收峰。 SPR峰显示出红移并随着Au含量从10到40 mol％的增加而增强，但是显示出蓝移并从40 mol％到60 mol％减弱。带隙E_g随着Au含量从10摩尔％增加到40摩尔％而减小，但是通过进一步增加Au含量而增加。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号