We report a single step growth of thin graphene-like, densely packed FeV3O8 (FVO) nanosheets on silicon substrates via facile hydrothermal synthesis. These nanosheets have dimensions of a few microns with thin edges, offering very high aspect ratio. These FVO nanosheets exhibit excellent field emission behaviour with low turn on and threshold voltages of 1.3 V mu m(-1) and 1.7 V mu m(-1), respectively. The corresponding emitter delivers high emission current density of (similar to 1.650 mA cm(-2)) at fairly low applied field (similar to 4.00 V mu m(-1)).
机译：我们报告了通过简便的水热合成在硅基底上一步一步生长的薄石墨烯状，紧密堆积的FeV3O8（FVO）纳米片。这些纳米片的尺寸为几微米，边缘较薄，具有很高的纵横比。这些FVO纳米片具有出色的场发射性能，其低导通电压和阈值电压分别为1.3 Vμm（-1）和1.7 Vμm（-1）。相应的发射器在相当低的施加电场（类似于4.00 Vμm（-1））下提供高发射电流密度（类似于1.650 mA cm（-2））。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号