X-ray absorption near edge structure investigation of iron-sodium silicate glasses

机译：铁 - 硅酸钠玻璃边缘结构附近的X射线吸收

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

X-ray absorption near edge structure spectroscopy has been used at the O K and Fe L2,3 edges to investigate the electronic and atomic structure of (Fe_2O_3)_x(Na_2O) _(0.30)(SiO_2)_(0.70 - x) (x < 0.2) obtained by melt-quench technique. The Fe L_(2,3) edge spectra show that the Fe atoms are in octahedral coordination. The O K edge spectra reveal no change in coordination of Fe and increased degree of hybridization between O 2p and Fe 3d orbitals with iron doping. It is estimated that about 10% Fe~(2+) and 90% Fe~(3+) are in these glasses by peak fitting analysis of Fe L _3 edge. The ligand-field splitting of Fe 3d orbital is about 1.6 eV.
机译：近边缘结构光谱附近的X射线吸收已经在OK和Fe L2,3边缘中使用，以研究（Fe_2O_3）_x（NA_2O）_（0.30）（SiO_2）_（0.70 - x）（x）的电子和原子结构（x <0.2）通过熔融淬火技术获得。 Fe L_（2,3）边缘光谱表明Fe原子是八面体的协调。 O K边缘光谱显示FE的协调和含铁掺杂的O 2P和FE 3D轨道之间的Fe和杂交程度的变化没有变化。 据估计，通过Fe L _3边缘的峰值分析，在这些眼镜中估计约10％Fe〜（2+）和90％Fe〜（3+）。 Fe 3D轨道的配体场分裂约为1.6eV。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号