首页> 外文期刊>Russian Chemical Bulletin >Hybrid azobenzene-doped nanoporous polymers derived from cubic octavinylsilsesquioxane
【24h】

Hybrid azobenzene-doped nanoporous polymers derived from cubic octavinylsilsesquioxane

机译：杂交三苯苯掺杂纳米多孔聚合物衍生自立方八仙戊酰基硅硅氧烷

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A series of novel hybrid porous polymers (HPPs) with high specific surface areas were first prepared by one-step ternary cross-linking copolymerization of octavinylsilsesquioxane (OVS), 1,3,5-tribromobenzene, and 4,4A '-dibromoazobenzene via the Heck reaction. The porosities and the CO2 uptake capacities of resulting azobenzene-doped porous polymers could be tuned by modulating the molar percentage of the azo units. At 273 K and 101 kPa, the sample with the specific surface area of similar to 700 m(2) g(-1) (data of Brunauer-Emmett-Teller (BET) surface area analysis) showed the highest CO2 uptake of 5.45 wt.% (1.20 mmol g(-1)) among the fabricated HPPs.
机译：通过一步三元交联共聚的八烷基硅基硅氧烷（OVS），1,3,5-三溴苯和4,4A'-二溴氮苯并脱氧苯并脱氧，首先制备具有高比表面积的一系列新型杂化多孔聚合物（HPP）。 哎呀反应。 通过调节偶氮单元的摩尔百分比，可以调节所得偶氮苯掺杂多孔聚合物的孔隙率和CO2吸收能力。 在273 k和101 kPa，具有与700米（2）g（-1）类似的比表面积的样品（Brunauer-emmett-teller（bet）表面积分析的数据）显示出最高的CO2摄取为5.45 wt 。％（1.20mmol g（-1））在制造的HPP中。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号