首页> 外文期刊>Nanotechnology >Thermopower measurements on individual 30 nm nickel nanowires
【24h】

Thermopower measurements on individual 30 nm nickel nanowires

机译：单个30 nm镍纳米线上的热功率测量

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The thermopower of individual, 30 nm in diameter, Ni nanowires is measured as a function of bath temperature in the range 4-300 K. Boundary scattering of phonons at low temperatures (< 50 K) inhibits any phonon drag effect, that in contrast is observed for bulk Ni. In the diffusion regime (> 50 K) the absolute values of the thermopower are found to be smaller than the bulk values. This finding can be explained semi-quantitatively by considering electron scattering at grain boundaries. Any interpretation of size dependent thermopower in nanoscale ferromagnetic materials needs to explicitly consider the above effects.
机译：直径为30 nm的镍纳米线的热功率随浴温的变化在4-300 K范围内进行测量。在低温（<50 K）下声子的边界散射会抑制任何声子拖曳效应，相比之下，观察到大量镍。在扩散状态（> 50 K）下，发现热功率的绝对值小于总体值。可以通过考虑晶界处的电子散射来半定量地解释这一发现。纳米铁磁材料中与尺寸有关的热功率的任何解释都必须明确考虑上述影响。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号