首页> 外文期刊>CERAMICS INTERNATIONAL >Multilayer low temperature co-fired M-type barium hexaferrites and BaO center dot (Nd1-xBix)(2)O-3 center dot 4TiO(2) dielectric ceramics
【24h】

Multilayer low temperature co-fired M-type barium hexaferrites and BaO center dot (Nd1-xBix)(2)O-3 center dot 4TiO(2) dielectric ceramics

机译：多层低温共烧M型钡铁氧体和BaO中心点（Nd1-xBox）（2）O-3中心点4 TiO（2）介电陶瓷

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this study, tungsten bronze BaO center dot (Nd1-xBix)(2)O-3 center dot 4TiO(2)(x=0, 0.1, and 0.2, BNBT) dielectric cofired with M-type barium ferrite Ba(Co,Ti)(x)Fe12-2xO19(x=1.2, BaM(Co,Ti)(1.2)) magnetic ceramic was prepared via a low temperature cofired process using Bi2O3-B2O3-SiO2-ZnO (BBSZ) glass as a sintering aid. The BBSZ glass effectively reduced the sintering temperatures of these dielectric and magnetic ceramics through liquid phase sintering. With different amounts of glass, the BNBT dielectric and BaM(Co,Ti)(1.2) magnetic materials were sintered at temperature between 900 and 1000 degrees C with no second phase detected through XRD. The dielectric-glass and magnetic-glass multilayer composites showed excellent microstructures and very promising space efficient LC devices after sintering at 950 degrees C. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
机译：在这项研究中，钨青铜BaO中心点（Nd1-xBix）（2）O-3中心点4TiO（2）（x = 0、0.1和0.2，BNBT）电介质与M型钡铁氧体Ba（Co，使用Bi2O3-B2O3-SiO2-ZnO（BBSZ）玻璃作为烧结助剂，通过低温共烧工艺制备了Ti）（x）Fe12-2xO19（x = 1.2，BaM（Co，Ti）（1.2））磁性陶瓷。 BBSZ玻璃通过液相烧结有效地降低了这些介电和磁性陶瓷的烧结温度。使用不同量的玻璃，在900到1000摄氏度之间的温度下烧结BNB​​T电介质和BaM（Co，Ti）（1.2）磁性材料，而没有通过XRD检测到第二相。介电玻璃和磁性玻璃多层复合材料在950摄氏度下烧结后显示出出色的微观结构和非常有前途的节省空间的LC设备。（C）2015 Elsevier Ltd和Techna Group S.r.l.版权所有。