BiFeO_3 (BFO) multiferroic materials in the crystalline phase require very delicate processing conditions. In order to fabricate a high quality BFO thick film, aerosol deposition (AD) was employed and the phase evolution and multiferroic properties of the film were investigated for different annealing temperatures. A BFO thick film annealed at 500℃ had a dielectric constant of 80 at 1 kHz and possessed ferroelectric characteristics. At an applied electric field of ～900 kV/cm, the remaining polarization and coercive field (E_c) were approximately 7.5 μC/cm~2 and 370 kV/cm, respectively. In addition, the BFO thick film fabricated via AD and annealed at 500℃ showed weak ferromagnetic behavior between -1250 Oe and +1250 Oe and was saturated at the higher magnetic field strength, showing ferromagnetic behavior.
机译：处于结晶相的BiFeO_3（BFO）多铁性材料需要非常精细的加工条件。为了制造高质量的BFO厚膜，采用了气溶胶沉积（AD）并研究了在不同退火温度下膜的相演化和多铁性。 500℃退火的BFO厚膜在1 kHz时的介电常数为80，并具有铁电特性。在〜900 kV / cm的施加电场下，剩余极化强度和矫顽力（E_c）分别约为7.5μC/ cm〜2和370 kV / cm。另外，通过AD制备并在500℃退火的BFO厚膜在-1250 Oe和+1250 Oe之间表现出弱的铁磁性能，并在较高的磁场强度下饱和，表现出铁磁性能。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号